What is A105 Socket Weld Tee
ASTM A105 Forged Fittings are well suited for use in pressure systems, especially if the application ranges between ambient to elevated temperature. Materials used in the manufacture of Forged A105 Weld Fittings have to be subjected to heat treatment.
ASTM A105 socket weld tees are a type of high-pressure tee pipe connection fittings that are mainly formed by pressing and forging blanks from round steel or steel ingots, and then machined by lathes. They have a T-shaped shape and can be divided into equal diameter tees and reducing tees.
Shanghai Zhucheng Pipe Fitting Manufacturing Co., Ltd. specializes in producing and selling socket tees in accordance with the American standard ASME B16.11.
Schedule Class of Socket Weld Tee
Type | EQUAL TEE、REDUCING TEE |
Size | 1/8"-4"/DN6-DN100 |
Pressure | CLASS 3000、6000、9000 |
Dimension of ASME B16.11 Socket Weld Tee
Nominal | Depth | Dimension | Wall Thickness | Center to Bottom of Socket | |||||
Cmin | A | ||||||||
Tee | |||||||||
DN | NPS | Jmin | B | 3000 | 6000 | 9000 | 3000 | 6000 | 9000 |
6 | 1/8 | 10 | 10.7 | 3.2 | 3.5 | 11 | 11 | ||
8 | 1/4 | 10 | 14.1 | 3.3 | 4 | 11 | 15 | ||
10 | 3/8 | 10 | 17.5 | 3.5 | 4.4 | 13 | 15 | ||
15 | 1/2 | 10 | 21.8 | 4.1 | 5.2 | 8.2 | 16 | 19 | 25 |
20 | 3/4 | 13 | 27.4 | 4.3 | 6.1 | 8.6 | 19 | 22 | 28 |
25 | 1 | 13 | 34.2 | 5 | 7 | 10 | 22 | 27 | 32 |
32 | 1-1/4 | 13 | 42.9 | 5.3 | 7 | 10.6 | 27 | 32 | 35 |
40 | 1-1/2 | 13 | 48.3 | 5.6 | 7.8 | 11.2 | 32 | 38 | 38 |
50 | 2 | 16 | 61.1 | 6.1 | 9.5 | 12.2 | 38 | 41 | 41 |
65 | 2-1/2 | 16 | 76.9 (73.8) | 7.7 | 12.5 | 41 | 57 | ||
80 | 3 | 16 | 89.8 | 8.3 | 13.8 | 57 | 64 | ||
100 | 4 | 19 | 115.5 | 9.4 | 66 | ||||
ASTM A105 Socket Weld Tee Matieral
The material used to make ASTM A105 socket weld tee is carbon steel that means owing to the specified material conforms to the chemistry what based on the carbon steel grade used to produce these fitting. Therefore, the content of alloy ants like carbon, copper, nickel, manganese, phosphorus, chromium, sulfur, silicon, molybdenum and vanadium present in the Threaded Fitting must be one that suits the application.
Chemical Composition
| CHEMICAL | LIMITS | C | Mn | P | S | Si | Cu | Ni | Cr | Mo | V |
| ASTM A105 | MIN | 0.60 | 0.10 | ||||||||
| MAX | 0.35 | 1.05 | 0.035 | 0.040 | 0.35 | 0.40 | 0.40 | 0.30 | 0.12 | 0.08 |
Mechanical Properties
| MATERIAL | T.S (MPA) | Y.S (MPA) | EL % | R/A % | HARDNESS |
| ASTM A105 | 485 min | 250 min | 22 min | 30 min | 197 max |
Socket Weld Tee Weight Reference
Dimension | A105 Socket Weld Tee | |||
DN | NPS | 3000 | 6000 | 9000 |
6 | 1/8 | 0.13 | 0.22 | - |
8 | 1/4 | 0.13 | 0.22 | - |
10 | 3/8 | 0.16 | 0.45 | - |
15 | 1/2 | 0.35 | 0.55 | 1.15 |
20 | 3/4 | 0.48 | 0.90 | 1.80 |
25 | 1 | 0.66 | 1.46 | 2.25 |
32 | 1¼ | 1.00 | 1.90 | 3.95 |
40 | 1½ | 1.40 | 2.80 | 4.87 |
50 | 2 | 2.00 | 3.70 | 8.89 |
65 | 2½ | 4.10 | - | - |
80 | 3 | 5.55 | - | - |
100 | 4 | 15.6 | - | - |
ASTM A105 Socket Weld Tee Inspection of ASME B16.11
What is A105 Socket Weld Tee
ASTM A105 Forged Fittings are well suited for use in pressure systems, especially if the application ranges between ambient to elevated temperature. Materials used in the manufacture of Forged A105 Weld Fittings have to be subjected to heat treatment.
ASTM A105 socket weld tees are a type of high-pressure tee pipe connection fittings that are mainly formed by pressing and forging blanks from round steel or steel ingots, and then machined by lathes. They have a T-shaped shape and can be divided into equal diameter tees and reducing tees.
Shanghai Zhucheng Pipe Fitting Manufacturing Co., Ltd. specializes in producing and selling socket tees in accordance with the American standard ASME B16.11.
Schedule Class of Socket Weld Tee
Type | EQUAL TEE、REDUCING TEE |
Size | 1/8"-4"/DN6-DN100 |
Pressure | CLASS 3000、6000、9000 |
Dimension of ASME B16.11 Socket Weld Tee
Nominal | Depth | Dimension | Wall Thickness | Center to Bottom of Socket | |||||
Cmin | A | ||||||||
Tee | |||||||||
DN | NPS | Jmin | B | 3000 | 6000 | 9000 | 3000 | 6000 | 9000 |
6 | 1/8 | 10 | 10.7 | 3.2 | 3.5 | 11 | 11 | ||
8 | 1/4 | 10 | 14.1 | 3.3 | 4 | 11 | 15 | ||
10 | 3/8 | 10 | 17.5 | 3.5 | 4.4 | 13 | 15 | ||
15 | 1/2 | 10 | 21.8 | 4.1 | 5.2 | 8.2 | 16 | 19 | 25 |
20 | 3/4 | 13 | 27.4 | 4.3 | 6.1 | 8.6 | 19 | 22 | 28 |
25 | 1 | 13 | 34.2 | 5 | 7 | 10 | 22 | 27 | 32 |
32 | 1-1/4 | 13 | 42.9 | 5.3 | 7 | 10.6 | 27 | 32 | 35 |
40 | 1-1/2 | 13 | 48.3 | 5.6 | 7.8 | 11.2 | 32 | 38 | 38 |
50 | 2 | 16 | 61.1 | 6.1 | 9.5 | 12.2 | 38 | 41 | 41 |
65 | 2-1/2 | 16 | 76.9 (73.8) | 7.7 | 12.5 | 41 | 57 | ||
80 | 3 | 16 | 89.8 | 8.3 | 13.8 | 57 | 64 | ||
100 | 4 | 19 | 115.5 | 9.4 | 66 | ||||
ASTM A105 Socket Weld Tee Matieral
The material used to make ASTM A105 socket weld tee is carbon steel that means owing to the specified material conforms to the chemistry what based on the carbon steel grade used to produce these fitting. Therefore, the content of alloy ants like carbon, copper, nickel, manganese, phosphorus, chromium, sulfur, silicon, molybdenum and vanadium present in the Threaded Fitting must be one that suits the application.
Chemical Composition
| CHEMICAL | LIMITS | C | Mn | P | S | Si | Cu | Ni | Cr | Mo | V |
| ASTM A105 | MIN | 0.60 | 0.10 | ||||||||
| MAX | 0.35 | 1.05 | 0.035 | 0.040 | 0.35 | 0.40 | 0.40 | 0.30 | 0.12 | 0.08 |
Mechanical Properties
| MATERIAL | T.S (MPA) | Y.S (MPA) | EL % | R/A % | HARDNESS |
| ASTM A105 | 485 min | 250 min | 22 min | 30 min | 197 max |
Socket Weld Tee Weight Reference
Dimension | A105 Socket Weld Tee | |||
DN | NPS | 3000 | 6000 | 9000 |
6 | 1/8 | 0.13 | 0.22 | - |
8 | 1/4 | 0.13 | 0.22 | - |
10 | 3/8 | 0.16 | 0.45 | - |
15 | 1/2 | 0.35 | 0.55 | 1.15 |
20 | 3/4 | 0.48 | 0.90 | 1.80 |
25 | 1 | 0.66 | 1.46 | 2.25 |
32 | 1¼ | 1.00 | 1.90 | 3.95 |
40 | 1½ | 1.40 | 2.80 | 4.87 |
50 | 2 | 2.00 | 3.70 | 8.89 |
65 | 2½ | 4.10 | - | - |
80 | 3 | 5.55 | - | - |
100 | 4 | 15.6 | - | - |
ASTM A105 Socket Weld Tee Inspection of ASME B16.11